Introduction to Ultrasonic Thickness Gauges

29 Apr.,2024

 

Introduction to Ultrasonic Thickness Gauges

If you want to learn more, please visit our website.

Introduction to Ultrasonic Thickness Gauges

For more than fifty years, ultrasonic thickness gauges have been used by quality control professionals to measure the thickness of a wide variety of products across a range of industries. This includes inspectors testing critical parts like aircraft turbine blades for wear and maintenance crews checking pipes and tanks for in-service corrosion. As hardware and software development has advanced over the years, ultrasonic thickness gauges have become powerful, reliable, and user-friendly tools. This tutorial describes how they work and what they are used for.

What Are Ultrasonic Thickness Gauges Used For?

Ultrasonic thickness gauges are often used to determine the thickness of a material where an inspector only has access to one side of the part, such as a pipe or tube, or where simple mechanical measurement is impossible or impractical due to the part’s size or access limitations. The fact that thickness measurements can quickly and easily be made from one side, with no need to cut parts, is one of the major advantages of this technology.

Virtually any common engineering material can be measured ultrasonically. Ultrasonic thickness gauges can be set up for metals, plastics, composites, fiberglass, ceramics, and glass. In-line or in-process measurement of extruded plastics and rolled metal is often possible, as is the measurement of individual layers or coatings in multilayer fabrications. Liquid levels and biological samples can also be measured. Ultrasonic gauging is always completely nondestructive, with no cutting or sectioning required. The range of measurement can be as large as 0.08 mm (0.003 in.) to 635 mm (25 in.) depending on material and transducer selection. Materials that are generally unsuitable for measurement with conventional ultrasonic gauges include wood, concrete, paper, and foam products.

Ultrasonic thickness gauges work by very precisely measuring how long it takes for a sound pulse that has been generated by a probe called an ultrasonic transducer to travel through a test piece. Because sound waves reflect from material boundaries, timing the echo from the far side of the test piece can be used to gauge its thickness, in the same way that radar or sonar measure distance. Resolution can be as fine as 0.001 mm or 0.0001 in.

Most ultrasonic thickness gauging applications use small, handheld transducers, but some complex geometries as well as in-line testing require noncontact transducers that focus a sound beam through a water column or bath. Measurements are essentially instantaneous and can be recorded on internal instrument data loggers for documentation or analysis.

What Materials Can Be Measured with an Ultrasonic Thickness Gauge?

Ultrasonic gauging can be used to measure corrosion, coatings, and a range of materials, most typically metals, plastics, composites, fiberglass, or ceramic glass.

Corrosion

If undetected over time, corrosion can weaken the structural integrity of metals like beams, bridge supports, and steel pilings. Ultrasonic thickness gauges can be used to nondestructively inspect metals to detect any damage or weakness that corrosion might have caused to metal structures.

Metals

Ultrasonic thickness gauges can be used to measure many metal products, including pipes and tanks, sheets and coils, gun drilling, or tubing. Ultrasonic gauging can be used for quality assurance purposes to ensure that manufacturing meets industry standards and that a product is safe and strong enough to perform its key function.

Plastics

The use of nonmetallic engineering products like plastics has become more common, increasing the need for wall thickness to be measured for quality control. Ultrasonic testing is now used on bottles and containers, plastic pipes, and fiberglass pipes and boats to ensure industry standards are accurately met and manufactured materials are safe to use.

Other Materials

Ultrasonic gauging can also be used for a variety of other materials. This includes rubber products, ceramics, glassware, and liquid level, where the user cannot access both sides of the material.

How is Coating Thickness Measured? | Resources

As seen in issues of: Canadian Finishing & Coating Mfg. Industrial Paint & Powder Magazine; Metal Finishing - Organic Finishing Guidebook

by David Beamish, DeFelsko Corporation
Updated: 09/13/2021

Coating thickness is an important variable that plays a role in product quality, process control, and cost control. Measurement of film thickness can be done with many different instruments. Understanding the equipment that is available for paint thickness measurement and how to use it is useful to every coating operation.

The issues that determine what method is best for a given paint or coating measurement include the type of coating, the substrate material, the thickness range of the coating, the size and shape of the part, and the cost of the equipment. Commonly used measuring techniques for cured organic films include nondestructive dry film methods such as magnetic, eddy current, ultrasonic, or micrometer measurement and also destructive dry film methods such as cross-sectioning or gravimetric (mass) measurement. Methods are also available for measuring paint and powder coating thickness before the film has cured.

What are Magnetic Paint Thickness Gauges?

Magnetic paint gages are used to nondestructively measure the thickness of a nonmagnetic coating on ferrous substrates. Most coatings on steel and iron are measured this way. Magnetic gages use one of two principles of operation: magnetic pull-off or magnetic/electromagnetic induction.

What are Magnetic Pull-off Paint Thickness Gauges?

Magnetic pull-off paint thickness gages use a permanent magnet, a calibrated spring, and a graduated scale. The attraction between the magnet and magnetic steel pulls the two together. As the coating thickness separating the two increases, it becomes easier to pull the magnet away. Paint and coating thickness is determined by measuring this pull-off force. Thinner coatings will have stronger magnetic attraction while thicker films will have comparatively less magnetic attraction. Testing with magnetic thickness gages is sensitive to surface roughness, curvature, substrate thickness, and the make up of the metal alloy.

Magnetic pull-off gages are rugged, simple, inexpensive, portable, and usually do not require any calibration adjustment. They are a good, low-cost alternative in situations where quality goals require only a few readings during production.

Magnetic Pull-off Paint Thickness gages are typically pencil-type or rollback dial models. Pencil-type models (PosiPen shown in Fig 1) use a magnet that is mounted to a helical spring that works perpendicularly to the coated surface. Most pencil-type pull-off coating thickness gages have large magnets and are designed to work in only one or two positions, which partially compensate for gravity. A more accurate version is available, which has a tiny, precise magnet to measure on small, hot, or hard-to-reach surfaces. A triple indicator ensures accurate measurements when the thickness gage is pointed down, up, or horizontally with a tolerance of ±10%.

Fig. 1. Pencil-type magnetic pull-off thickness gauge.

Rollback dial models (PosiTest shown in Fig 2) are the most common form of magnetic pull-off gage. A magnet is attached to one end of a pivoting balanced arm and connected to a calibrated hairspring. By rotating the dial with a finger, the spring increases the force on the magnet and pulls it from the surface. These paint thickness gages are easy to use and have a balanced arm that allows them to work in any position, independent of gravity. They are safe in explosive environments and are commonly used by painting contractors and small powder coating operations. Typical tolerance is ±5%.

Fig. 2. Roll-back dial magnetic pull-off thickness gauge.

DeFelsko manufactures 2 pull-off paint thickness meters, the PosiPen and PosiTest.

What are Magnetic and Electromagnetic Induction Paint Thickness Gauges?

Magnetic induction paint meters use a permanent magnet as the source of the magnetic field. A Hall-effect generator or magneto-resistor is used to sense the magnetic flux density at a pole of the magnet. Electromagnetic induction paint meters use an alternating magnetic field. A soft, ferromagnetic rod wound with a coil of fine wire is used to produce a magnetic field. A second coil of wire is used to detect changes in magnetic flux.

These electronic paint meters measure the change in magnetic flux density at the surface of a magnetic probe as it nears a steel surface. The magnitude of the flux density at the probe surface is directly related to the distance from the steel substrate. By measuring flux density the coating thickness can be determined.

Fig. 3. Electronic magnetic induction thickness gauges.

Electronic magnetic thickness gages (e.g. PosiTector 6000 F Series, PosiTest DFT Ferrous) come in many shapes and sizes. They commonly use a constant pressure probe to provide consistent readings that are not influenced by different operators. Paint mil thickness readings are shown on a liquid crystal display (LCD). Paint mil gauges can have options to store measurement results, perform instant analysis of readings, and output results to a printer or computer for further examination. Typical tolerance is ±1%.

The manufacturer’s instructions should be carefully followed for most accurate results. Standard test methods are available in ASTM D 1186, D 7091-05, ISO 2178, and ISO 2808.

What are Eddy Current Paint Thickness Gauges?

Eddy current techniques are used to nondestructively measure the thickness of nonconductive coatings on nonferrous metal substrates. A coil of fine wire conducting a high-frequency alternating current (above 1 MHz) is used to set up an alternating magnetic field at the surface of the instrument's probe. When the coating thickness probe is brought near a conductive surface, the alternating magnetic field will set up eddy currents on the surface. The substrate characteristics and the distance of the probe from the substrate (the coating thickness) affect the magnitude of the eddy currents. The eddy currents create their own opposing electromagnetic field that can be sensed by the exciting coil or by a second, adjacent coil.

Eddy current coating thickness gages (e.g. PosiTector 6000 N Series) look and operate like electronic magnetic gages. They are used to measure paint and coating thickness over all nonferrous metals. Like magnetic electronic gages, they commonly use a constant pressure probe and display results on an LCD. They can also have options to store measurement results or perform instant analysis of readings and output to a printer or computer for further examination. The typical tolerance is ±1%. Testing is sensitive to surface roughness, curvature, substrate thickness, type of metal substrate, and distance from an edge.

With competitive price and timely delivery, AJR sincerely hope to be your supplier and partner.

Standard methods for the application and performance of this test are available in ASTM B244, ASTM D1400, D7091, and ISO 2360.

It is now common for paint thickness meters to incorporate both magnetic and eddy current principles into one unit (e.g. PosiTector 6000 FN, PosiTest DFT Combo). Some simplify the task of measuring most coatings over any metal by switching automatically from one principle of operation to the other, depending upon the substrate. These combination paint mil gauges are popular with painters and powder coaters.

What are Ultrasonic Paint Thickness Gauges?

The ultrasonic pulse-echo technique of ultrasonic paint thickness gages (e.g. PosiTector 200) is used to measure the thickness of coatings on nonmetal substrates (plastic, wood, etc.) without damaging the coating.

Fig. 4. Ultrasonic paint thickness gauges can measure the thickness of coatings on nonmetallic substrates.

The probe of the paint meter contains an ultrasonic transducer that sends a pulse through the coating. The pulse reflects back from the substrate to the transducer and is converted into a high frequency electrical signal. The echo waveform is digitized and analyzed to determine coating thickness. In some circumstances, individual layers in a multi-layer system can be measured.

Typical tolerance for this device is ±3%. Standard methods for the application and performance of this test are available in ASTM D6132.

For further reading about Ultrasonic Paint Thickness Gauges, please see, "Using Ultrasonic Coating Thickness Gages".

How are Micrometers Used for Paint Thickness Measurement?

Micrometers are sometimes used to check coating thickness. They have the advantage of measuring any coating/substrate combination but the disadvantage of requiring access to the bare substrate. The requirement to touch both the surface of the coating and the underside of the substrate can be limiting and they are often not sensitive enough to measure thin coatings.

Two measurements must be taken: one with the coating in place and the other without. The difference between the two readings, the height variation, is taken to be the coating thickness. On rough surfaces, micrometers measure coating thickness above the highest peak.

What Destructive Tests are Used for Paint Thickness Measurement?

One destructive technique is to cut the coated part in a cross section and measure the film thickness by viewing the cut microscopically. Another cross sectioning technique uses a scaled microscope to view a geometric incision through the dry-film coating. A special cutting tool is used to make a small, precise V-groove through the coating and into the substrate. Gages are available that come complete with cutting tips and illuminated scaled magnifier.

While the principles of this destructive method are easy to understand, there are opportunities for measuring error. It takes skill to prepare the sample and interpret the results. Adjusting the measurement reticule to a jagged or indistinct interface may create inaccuracy, particularly between different operators. This method is used when inexpensive, nondestructive methods are not possible, or as a way of confirming nondestructive results. ASTM D 4138 outlines a standard method for this measurement system.

What is the Gravimetric Method for Paint Thickness Measurement?

By measuring the mass and area of the coating, thickness can be determined. The simplest method is to weigh the part before and after coating. Once the mass and area have been determined, the thickness is calculated using the following equation:

where T is the thickness in micrometers, m is the mass of the coating in milligrams, A is the area tested in square centimeters, and d is the density in grams per cubic centimeter.

It is difficult to relate the mass of the coating to thickness when the substrate is rough or the coating uneven. Laboratories are best equipped to handle this time-consuming and often destructive method.

How Do You Measure Paint Thickness Before Cure?

Wet-film thickness gauges help determine how much material to apply wet to achieve a specified dry-film thickness provided that the percent of solids by volume is known. They measure all types of wet organic coatings, such as paint, varnish, and lacquer on flat or curved smooth surfaces.

Measuring wet film thickness during application identifies the need for immediate correction and adjustment by the applicator. Correction of the film after it has dried or chemically cured requires costly extra labor time, may lead to contamination of the film, and may introduce problems of adhesion and integrity of the coating system.

The equations for determining the correct wet-film thickness (WFT), both with and without thinner, are as follows:

Without thinner:

With thinner:

Wet-film is most often measured with a wet film comb or wheel. The wet-film comb is a flat aluminum, plastic, or stainless steel plate with calibrated notches on the edge of each face. The gage is placed squarely and firmly onto the surface to be measured immediately after coating application and then removed. The wet-film thickness lies between the highest coated notch and the next uncoated notch. Notched gage measurements are neither accurate nor sensitive, but they are useful in determining approximate wet-film thickness of coatings on articles where size and shape prohibit the use of more precise methods. (ASTM D1212).

The gage should be used on smooth surfaces, free from irregularities and should be used along the length, not the width, of curved surfaces. Using a wet-film gage on quick-drying coatings will yield inaccurate measurements. ASTM D4414 outlines a standard method for measurement of wet-film thickness by notch gages.

A wet film wheel (eccentric roller) uses three disks. The gage is rolled in the wet film until the center disk touches the wet film. The point where it makes contact provides the wet film thickness.Powder coatings can be measured prior to curing with a simple hand-held comb or an ultrasonic gage. The uncured powder film comb works much the same way as wet film gage. The comb is dragged through the powder film and the thickness lies between the highest numbered tooth which made a mark and has powder clinging to it, and the next highest tooth which left no mark and has no powder clinging to it. These gages are relatively inexpensive with accuracy of ±5mm. They are only suitable as a guide since the cured film may be different after flow. Marks left by the gage may affect the characteristics of the cured film.

An ultrasonic device, such as the PosiTest PC, can be used non-destructively on uncured powder on smooth metallic surfaces to predict the thickness of the cured film. The probe is positioned a short distance from the surface to be measured and a reading is displayed on the LCD of the device. Measurement uncertainty is ±5mm.

Coating Thickness Standards

 

Coating thickness gages are calibrated to known thickness standards. There are many sources of thickness standards but it is best to ensure they are traceable to a national measurement institute such as NIST (National Institute of Standards & Technology). It is also important to verify the standards are at least four times as accurate as the gage they will be used to calibrate. A regular check against these standards verifies the gage is operating properly. When readings do not meet the accuracy specification of the gage, the gage must be adjusted or repaired and then calibrated again.

Summary

Film thickness in coatings can have a big impact on cost and quality. Measurement of film thickness should be a routine event for all coaters. The correct paint meter to use depends on the thickness range of the coating, the shape and type of substrate, the cost of the paint meter, and how critical it is to get an accurate measurement. 

DAVID BEAMISH (1955 – 2019), former President of DeFelsko Corporation, a New York-based manufacturer of hand-held coating inspection instruments sold worldwide. He had a degree in Civil Engineering and more than 25 years of experience in the design, manufacture, and marketing of these testing instruments in a variety of international industries including industrial painting, quality inspection, and manufacturing. He conducted training seminars and was an active member of various organizations including NACE, SSPC, ASTM and ISO.